MIRAFI® H2Ri was installed on Flat Creek Drive in Jackson, Wyoming, to stabilize the subgrade and manage moisture from snowmelt, preventing pavement damage and extending roadway life.
Reflective cracking on airport pavements can lead to fatigue and premature cracking in the surface layer, making the pavements susceptible to further damage from moisture infiltration and traffic loading. One of the tarmacs at DeKalb-Peachtree Airport experienced cracking, prompting DeKalb County to rehabilitate the pavement. The project engineer decided to incorporate an asphalt interlayer due to the higher strength of the cement-treated base (CTB) than anticipated, which increased the risk of shrinkage cracking. To prevent premature reflective cracking, it was recommended to use a paving fabric between the CTB and the asphalt layers. The contractor had two options: either remove and replace the CTB or utilize a 4 oz/sq yd (118 g/sq m) nonwoven paving fabric. They selected Petromat MPV600, a 4.6 oz/sq yd (136 g/sq m) nonwoven fabric known for effectively reducing the risk of reflective cracking. When saturated with asphalt liquid, Petromat MPV600 forms a stress-absorbing crack relief membrane and moisture barrier.
The proposed pavement section consisted of two asphalt layers on top of the aggregate cement-treated base, making the typical placement location for the paving fabric between the two asphalt layers. In asphalt or flexible pavements, tensile strains increase with depth, so the most optimal position for the paving fabric is at the lowest point in the asphalt. Therefore, to achieve the best life cycle performance, Petromat MPV600 was installed directly on the CTB, providing protection to both overlaying layers of the asphalt. This approach had not been used historically because it was considered too messy to be a sustainable surface for installation. However, this project demonstrated that installation on a CTB can be successfully carried out.
Approximately 11,000 yd² (9,197 m²) of Petromat MPV600 was installed on a section of the airport’s pavement. The maximum ambient temperature during installation was 65 degrees Fahrenheit (18 degrees Celsius), and the chosen asphalt binder was a PG64-22. The application rate of the asphalt binder was approximately 0.28 gal/sy (1.37 L/m²). Placing the paving fabric directly on the CTB expedited the installation process and ensured the interlayer could remain in service for future rehabilitations.
Petromat MPV600 will serve as a long-term moisture barrier for the airport pavement, mitigating reflective cracking and preventing surface water from penetrating into the subgrade.
The fabric extends pavement lifespan
Petromat MPV600 is installed on the CTB
Flat Creek Drive road rehab with MIRAFI H2Ri
MIRAFI® H2Ri was installed on Flat Creek Drive in Jackson, Wyoming, to stabilize the subgrade and manage moisture from snowmelt, preventing pavement damage and extending roadway life.
Geosynthetic reinforcement enables fast-tracked yard expansion
A geosynthetic reinforcement solution using MIRAFI RSi enabled the expansion of a 140-acre laydown yard in Pueblo, Colorado, reducing aggregate needs and meeting a fast-tracked construction schedule despite poor soil and remote material sources.
Subgrade stabilization for fuel containment at Naval Base Point Loma
At the Point Loma naval base, Solmax stabilized soft subgrade for fuel tank containment dyke walls using MIRAFI RS580i, crushed stone, and geogrid reinforcement.